Product Details:
Payment & Shipping Terms:
|
| Product Name: | High Performance Polyurethane Windshiled Adhesive | Volume: | Cartridge Packing/sausage Packing/drum Packing |
|---|---|---|---|
| Color: | Black | Application Method: | Extruding |
| Brand: | Aristo/OEM | Shelf Life: | 9 Months In Dry And Cool Place |
| High Light: | Windshiled Adhesive Polyurethane Sealant,20ml/Min Polyurethane Sealant,6.0Mpa Pu Adhesive Sealant |
||
Description:
Aristo High strength PU Sealant for Car factories is high quality, one-part, non-sag, polyurethane sealant that cures by reaction with atmospheric moisture to form a durable and weathering resistant elastomer. It is manufactured in accordance with the ISO/TS 16949:2002.
Applications:
Features:
Technical Data:
| Item | Range | Typical value |
| Appearance | Black, homogenous paste | Black |
|
Extrudability (ml/min) GB/T13477.4 |
≥20 | 30 |
|
Sagging Properties (mm) GB/T13477.6 |
0 | 0 |
|
Tack free time (min) GB/T 13477.5 |
10~40 | 20 |
|
Curing speed (mm/d) HG/T 4363 |
≥3.0 | 3.5 |
| Non-volatile matter content (%) GB/T 2793 | ≥97 | 98 |
|
Shore A – hardness GB/T 531.1 |
50~60 | 56 |
|
Tensile strength (Mpa) GB/T 528 |
≥6.0 | 6.8 |
|
Elongation at break (%) GB/T 528 |
≥400 | 460 |
|
Tear strength (N/mm) GB/T 529 |
≥8.0 | 10.2 |
| Tensile-shear strength (Mpa) GB/T 7124 | ≥3.5 | 4.2 |
| Tensile-shear for 4 hour strength (Mpa) HG/T4363 | ≥0.1 | 0.3 |
|
Operating Temperature (ºC): |
-40~90 | |
Note: All data above were tested under standardized condition
Regular Colors: Black
Packing:
Cartridge Package: 310ml x 20/carton or 310ml x 12/carton
Sausage Packing: 600ml x20/carton
Drum Packing: 200Liter/drum
Shelf Life: 9 months in dry and cool place
Contact Person: Mrs. Cherry Zhang
Tel: 86-755-22214189--805
Fax: 86-755-22214186
| Factory Address:Refined Chemical Industrial Zone,Overseas Chinese Park,Yingde City,Guangdong Province,PRC,513059,China | |
| Sales office:501-502, Qiurui Bldg., Minkang Rd., Minzhi, Longhua, Shenzhen, China | |
| +86-755-22214189 | |
| cherry@aristoindustries.com | |